Titanium 8-1-1 (8Al-1Mo-1V) is a near alpha alloy offering good weldability and with superior creep resistance at operating temperature up to 450°C. Alloy 8-1-1 has a relatively high tensile modulus to density ratio and is used primarily in engine applications such as forged compressor blades and disks.
Standard Specification:
AMS-T-9047 8Al-1Mo-1v bar;
MIL-T-9047G 8Al-1Mo-1V bar;
Standard |
Werkstoff No. |
UNS |
AMS Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
3.7134 |
R54810 |
Technical Data Sheet
Chemical Composition |
||||||||||
Weight % |
Ti |
Al |
Mo |
V |
C |
Fe |
N |
O |
H |
Other |
AMS Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
Balance |
7.35~8.35 |
0.75~1.25 |
0.75~1.25 |
0.08 |
0.30 |
0.05 |
0.2 |
0.0150 |
0.4 Total Max. |
Typical Mechanical Properties (Tensile Requirements)
Material |
Tensile Strength, min |
Yield Strength (0.2% Offset) min or range |
Elongation in 4D,min% |
eduction of Area Min % |
||
ksi |
MPa |
ksi |
MPa |
|||
Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
130 |
896 |
120 |
827 |
10 |
20 |
1. TitaniumRodfor Neurosurgery Implants KirschnerRod Specification (mm) Φ7mm~Φ230mm Length (mm) 1000~3000
Standard Specification: ASTM B348, ASME SB348, ISO, DINAWS A5.16 (ERTi-36); Standard Werkstoff No. UNS Titanium Al
Titanium Alloy Grade 12 is lightly alloyed near-alpha alloy offering improved strength at elevated temperatures and optimum ASME Code design allowables. The material is readily weldable, and
Titanium Alloy Grade9 Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness. It is used in a wide range of tubular pro