Titanium alloy Grade 9 Ti-3Al-2.5V Bar and Rod

1.Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness.
2.Size: Φ7mm~Φ230mm;

Products Inquiry

CompanyName * :

Email * :

Name :

Tel :

Message :

Product Details

Titanium Alloy Grade9 Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness. It is used in a wide range of tubular products from aircraft ducting to golf club shafts and bicycle frames. The alloy is available as wire, bar, sheet, seamless and welded tubing. ASME code approved.

Standard Specification: ASTM B348, ASME SB348, , ISO, DIN

Standard	Werkstoff No.	UNS
Titanium Alloy Grade9 Ti-3Al-2.5V	3.7195	R56320

Technical Data Sheet

Chemical Composition
Weight %	Ti	Al	V	C	Fe	N	O	H
Titanium Alloy Grade9 Ti-3Al-2.5V	Balance	2.5~3.5	2.0~3.0	0.08	0.25	0.03	0.15	0.015

Typical Mechanical Properties (Tensile Requirements)

Material

Tensile Strength, min

Yield Strength (0.2% Offset) min or range

Elongation in 4D,min%

Reduction of Area

Min %

ksi

MPa

ksi

MPa

Titanium Alloy Grade9 Ti-3Al-2.5V

620

483

AMS Titanium Alloy 6-2-4-2 (6Al-2Sn-4Zr-2Mo) Bar and Rod

Titanium 6-2-4-2 (6Al-2Sn-4Zr-2Mo) is an alpha-beta titanium alloy capable of being heat treated to higher strengths in greater section sizes that 6Al-4V. Widely used in forged components, 6-2-4-2 be

Titanium alloy Grade 7 Ti-0.2Pd Bar and Rod

Titanium Alloy Grade 7 with 0.1% palladium is similar to Grade 2, but with improved resistance to general and localized crevice corrosion in a wide range of reducing acid environments, incl

Titanium Alloy Grade23 Ti-6Al-4VELI (Extra low interstitials) Bar and Rod

Ti-6Al-4V alloy is the most widely used titanium alloy of the alpha-plus beta class, and is also the most common of all titanium alloys. This modification incorporates extra low inters

Titanium Alloy Grade5 Ti-6Al-4V Bar and Rod